GENERAL DESCRIPTIONKETRON ® PEEK-CA30 LSG PolyEtherEtherKetone stock shapes are produced from genuine Victrex ® PEEK polymer. This 30% carbon fiber-reinforced grade combines even higher stiffness, mechanical strength and creep resistance than KETRON ® PEEK-GF30 LSG blue with an optimum wear resistance.
KETRON PEEK-CA30 LSG stock shapes have been successfully type tested for their compliance with both United States Pharmacopeia (USP) and ISO 10993-1 guideline requirements for Biocompatibility Testing of Materials, and they come with full traceability from resin to stock shape. These features, added to an excellent sterilizability by means of steam, dry heat, ethylene oxide, plasma and gamma irradiation, make KETRON PEEK-CA30 LSG stock shapes very suitable for applications in the medical, pharmaceutical and biotechnology markets.
Ketron PEEK-CA30 LSG is available in sheet and rod forms in black color only.
Quadrant's PEEK-CA30 Life Science Grade should not be used for applications involving medical devices that are intended to remain implanted in the human body continuously for a period exceeding 24 hours, or are intended to remain in contact with internal human tissue or bodily fluids for more than 24 hours, or as critical components of medical devices that are essential to the continuation of human life.
Other Medical "Life Science Grade" Products:
Ketron PEEK LSG | Ketron PEEK-GF30 LSG | Ketron PEEK-CLASSIX LSG | Techtron HPV LSG
( see also Standard PEEK PolyEtherEtherKetone Specifications )
TYPICAL PROPERTIES of KETRON® PEEK-CA30 LSG
|Property||Ketron® PEEK-CA30 LSG|
|62||Water Absorption, 24 hrs (%)||0.05|
|527||Tensile Strength (psi / MPa)||20,900 / 144|
|527||Tensile Modulus (psi / MPa)||1,335,000 / 9,200|
|527||Tensile Elongation at Break (%)||5|
|178||Flexural Strength (psi / MPa)||34,800 / 240|
|178||Flexural Modulus (psi / MPa)||-|
|-||Compressive Strength (psi / MPa)||-|
|-||Compressive Modulus (psi / MPa)||-|
|2039-2||Hardness, Rockwell||M 102|
|179-1/1eA||Charpy Notched Impact (kJ/m2)||5|
|-||Coefficient of Linear Thermal Expansion
(x 10-5 in./in./°F)
(x 10-5 mm/mm/°K)
|75||Heat Deflection Temp (°F / °C)
at 264 psi / 1.8 MPa
464 / 240
|11357||Melting Temp (°F / °C)||644 / 340|
|-||Max Operating Temp (°F / °C)||480 / 250|
|(60243)||Dielectric Strength (kV/mm) short time||-|
|(60250)||Dissipation Factor at 1 MHz||-|
|(60093)||Surface Resistivity (ohm-cm)||< 105|
|(60093)||Volume Resistivity (ohm-cm)||< 105|
NOTE: The information contained herein are typical values intended for reference and comparison purposes only. They should NOT be used as a basis for design specifications or quality control. Contact us for manufacturers' complete material property datasheets.KETRON and TECHTRON are registered trademarks of Quadrant Engineering Plastic Products.
All values at 73°F (23°C) unless otherwise noted.